1、The composite displays the fracture features of the dimple and intergranular fracture.
復(fù)合材料的斷裂形貌為韌窩加沿晶斷裂。

2、The intergranular cracking in relieved-stress annealing samples is not obvious.
去應(yīng)力退火試樣上發(fā)現(xiàn)了平行軋面的深溝，且沿晶開(kāi)裂不明顯。

3、The reason of intergranular corrosion and exfoliation corrosion is analyzed.
分析了發(fā)生晶間腐蝕和剝蝕的原因。

4、The indentation cracks propagation is typified by an intergranular and transgranular mixed mode.
壓痕裂紋擴(kuò)展為沿晶和穿晶混合模式。

5、The corrosion of poor Cu area is the root of intergranular corrosion.
貧銅區(qū)受到腐蝕是晶間腐蝕的根源。

6、These lath martensite first nucleates in parent austenite intergranular and twin boundary.
應(yīng)變誘發(fā)馬氏體首先在原奧氏體晶界和孿晶界形核。

7、The fracture surface appeared intergranular crack, due to the oxide formed during tensile test.
拉伸過(guò)程中形成的氧化物夾雜成為裂紋源，斷口表現(xiàn)為沿晶斷裂。

8、The pore categoryincludes micropore, intergranular pore and dissolved pore.
孔隙類型包括微孔、粒間孔和溶孔。